Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al | Others |
2024 | 0.5 | 0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-0.8 | 0.1 | 0.25 | 0.15 | Reminder | 0.1 |
2014 | 0.5-1.2 | 0.7 | 3.9-5.0 | 0.4-1.2 | 0.2-0.8 | 0.1 | 0.25 | 0.15 | Reminder | 0.15 |
Product | Temper | Specified thickness
mm | Tensile strength
Rm
MPa | Yeild strength
Rp0.2
MPa | Elongation min.
%
| Bend radius | Hardness HBWa | |||||
over | up to | min. | max. | min. | max. | A50min | A | 180° | 90° |
| ||
2024 | O | ≥0.4 | 1.5 |
| 220 |
| 140 | 12 |
| 0.5t | 0t | 55 |
1.5 | 3.0 |
| 220 |
| 140 | 13 |
| 2.0t | 1.0t | 55 | ||
3.0 | 6.0 |
| 220 |
| 140 | 13 |
| 3.0t | 1.5t | 55 | ||
6.0 | 9.0 |
| 220 |
| 140 | 13 |
|
| 2.5t | 55 | ||
9.0 | 12.5 |
| 220 |
| 140 | 13 |
|
| 4.0t | 55 | ||
12.5 | 25.0 |
| 220 |
|
|
| 11 |
|
| 55 | ||
T351 T4 | ≥0.4 | 1.5 | 425 |
| 275 |
| 12 |
| 4.0t |
| 120 | |
1.5 | 6.0 | 425 |
| 275 |
| 14 |
| 5.0t |
| 120 | ||
T3 | ≥0.4 | 1.5 | 435 |
| 290 |
| 12 |
| 4.0tb | 4.0tb | 123 | |
1.5 | 3.0 | 435 |
| 290 |
| 14 |
| 4.0tb | 4.0tb | 123 | ||
3.0 | 6.0 | 440 |
| 290 |
| 14 |
| 5.0tb | 5.0tb | 124 | ||
6.0 | 12.5 | 440 |
| 290 |
| 13 |
|
| 8.0tb | 124 | ||
12.5 | 40.0 | 430 |
| 290 |
|
| 11 |
|
| 122 | ||
40.0 | 80.0 | 420 |
| 290 |
|
| 8 |
|
| 120 | ||
80.0 | 100.0 | 400 |
| 285 |
|
| 7 |
|
| 115 | ||
100.0 | 120.0 | 380 |
| 270 |
|
| 5 |
|
| 110 | ||
120.0 | 150.0 | 360 |
| 250 |
|
| 5 |
|
| 104 | ||
2014 | T4 T451 | ≥0.4 | 1.5 | 395 |
| 240 |
| 14 |
| 3.0t | 3.0t | 110 |
1.5 | 6.0 | 395 |
| 240 |
| 14 |
| 5.0t | 5.0t | 110 | ||
6.0 | 12.5 | 400 |
| 250 |
| 14 |
|
| 8.0t | 112 | ||
12.5 | 40.0 | 400 |
| 250 |
|
| 10 |
|
| 112 | ||
40.0 | 100.0 | 395 |
| 250 |
|
| 7 |
|
| 111 | ||
T6 T651 | ≥0.4 | 1.5 | 440 |
| 390 |
| 6 |
|
| 5.0t | 133 | |
1.5 | 6.0 | 440 |
| 390 |
| 7 |
|
| 7.0t | 133 | ||
6.0 | 12.5 | 450 |
| 395 |
| 7 |
|
| 10t | 135 | ||
12.5 | 40.0 | 460 |
| 400 |
|
| 6 |
|
| 138 | ||
40.0 | 60.0 | 450 |
| 390 |
|
| 5 |
|
| 135 | ||
60.0 | 80.0 | 435 |
| 380 |
|
| 4 |
|
| 131 | ||
80.0 | 100.0 | 420 |
| 360 |
|
| 4 |
|
| 126 | ||
100.0 | 125.0 | 410 |
| 350 |
|
| 4 |
|
| 123 | ||
125.0 | 160.0 | 390 |
| 340 |
|
| 2 |
|
|
Aerospace Applications
Aircraft Structures: Wings, fuselage skins, bulkheads, and other structural components due to high strength-to-weight ratio and fatigue resistance.
Spacecraft Components: Used in parts requiring durability under stress without excessive weight.
Automotive Industry
High-Performance Vehicles: Suspension systems, chassis parts, and racing components where strength and weight savings are critical.
Pistons and Engine Parts: Heat-treated 2xxx alloys for durability under thermal stress.
Machinery and Tooling
Jigs and Fixtures: Precision tooling plates requiring dimensional stability.
Gears and Shafts: Machined parts benefiting from high machinability (e.g., alloy 2011).
Transportation
Rail and Truck Components: Structural parts where weight reduction is prioritized (with corrosion protection).
Industrial Applications
Fasteners and Bolts: Machined from plates due to excellent machinability (e.g., 2011).
Hydraulic Systems: High-pressure components requiring strength.
Sporting Goods
Bicycle Frames/Racing Components: Lightweight, high-strength parts (often anodized for corrosion resistance).
Climbing Gear: Carabiners and mounts treated for durability.
Repair and Maintenance
Aircraft Replacement Parts: Plates machined into specific components for repairs.
Key Considerations:
Joining Methods: Riveting or bolting preferred over welding due to poor weldability.
Corrosion Protection: Anodizing or coatings are essential for harsh environments.
These applications leverage the 2 series’ strength, machinability, and fatigue resistance, making them ideal for high-stress, lightweight scenarios where corrosion can be managed.
Request a personalized quote for premium aluminum products tailored to your project needs at Henan Victor.